I-Resin Coated Ceramic Sand
Incazelo
Isihlabathi se-ceramic sisetshenziswa esihlabathini sokubumba kanye nesihlabathi esiyinhloko ukwenza isikhunta segobolondo kanye negobolondo legobolondo libe nezindawo zokumelana nokushisa okuphezulu, ukunwetshwa okuphansi, ukuwa kalula, nokukhishwa kwegesi ephansi, okungavimbela ngokuphumelelayo ukukhubazeka kokunwetshwa kokusakazwa.Kuma-cores anezimo eziyinkimbinkimbi ikakhulukazi, angabhekana nenkinga yokuthi ukudubula kwesihlabathi akulula ukuhlanganisa.Kuyisihlabathi se-ceramic esisebenza kwinqubo ye-RCS.
Isihlabathi se-ceramic esigcwele sisetshenziselwa ukwenza isihlabathi esimboziwe, futhi siphinde sisetshenziswe ngokuphindaphindiwe ngemva kokubuyiselwa kabusha, okungathuthukisa ngempumelelo ikhwalithi nokusebenza kahle kokukhiqizwa kokusakazwa, ukunciphisa izinga le-castings scrape kanye nezindleko zokukhiqiza zamabhizinisi, izindleko zokusebenzisa isikhathi eside ziphansi kunalokho. ngesihlabathi se-silica.Ngakho-ke, eminyakeni yamuva, cishe zonke izitshalo zesihlabathi ezimbozwe ngezinga elikhulu ziye zasebenzisa isihlabathi sobumba njengesihlabathi esingavuthiwe ukukhiqiza isihlabathi esimboziwe.
Izici
• I-refractoriness ephakeme—-ukuphonsa izinsimbi ezinezinga lokushisa eliphezulu lokuthela (insimbi ekhonjiwe, insimbi eyingxubevange, insimbi engagqwali, njll.)
• Amandla aphezulu kanye nokuqina—–ukukhiqiza ama-cores ayinkimbinkimbi anezingxenye ezincane.
• Ukwehliswa kwe-thermal ephansi—–ukuze ugweme izinkinga zokunwetshwa.
• Isivuno esiphezulu sokubuyisela kabusha—-ukunciphisa ukulahlwa kwesihlabathi, ukwehlisa izindleko.
• Ukugeleza okuhle kakhulu —–ukwenza ama-cores ayinkimbinkimbi.
• Ukusetshenziswa okuphansi kwe-binder—–ukuvela kwegesi okuphansi, izindleko zokukhiqiza eziphansi.
• Izici zamakhemikhali angasebenzi—–zingasetshenziswa kunoma iyiphi ingxubevange edumile, ehlanganisa insimbi yeManganese.
• Isikhathi eside sokulondoloza.
I-Ceramic Sand Property e-RCS (Tiypical)
Okuqukethwe kwe-resin, % | 1.8%, |
Amandla e-Room Tensile, i-MPa | 6.78 |
Amandla okugoba ashisayo, i-MPa | 4.51 |
Amandla okugoba egumbi, i-MPa | 12.75 |
Iphuzu lokuncibilika, | 97℃ |
Ukuguquguquka kwegesi, ml/g | 13.6 |
LOI | 2.28% |
Ukunwetshwa komugqa | 0.14% |
Isikhathi sokuphumula | 40-60S |
GFN | AFS 62.24 |
Ukusabalalisa Usayizi Wokusanhlamvu
I-Mesh | 20 | 30 | 40 | 50 | 70 | 100 | 140 | 200 | 270 | Ipani | Ububanzi be-AFS |
μm | 850 | 600 | 425 | 300 | 212 | 150 | 106 | 75 | 53 | Ipani | |
#400 | ≤5 | 15-35 | 35-65 | 10-25 | ≤8 | ≤2 | 40±5 | ||||
#500 | ≤5 | 0-15 | 25-40 | 25-45 | 10-20 | ≤10 | ≤5 | 50±5 | |||
#550 | ≤10 | 20-40 | 25-45 | 15-35 | ≤10 | ≤5 | 55±5 | ||||
#650 | ≤10 | 10-30 | 30-50 | 15-35 | 0-20 | ≤5 | ≤2 | 65±5 | |||
#750 | ≤10 | 5-30 | 25-50 | 20-40 | ≤10 | ≤5 | ≤2 | 75±5 | |||
#850 | ≤5 | 10-30 | 25-50 | 10-25 | ≤20 | ≤5 | ≤2 | 85±5 | |||
#950 | ≤2 | 10-25 | 10-25 | 35-60 | 10-25 | ≤10 | ≤2 | 95±5 |